Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Tubes

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Elektro-Isola
Trade Name	G-Etronax
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Tubes.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Used in mechanical, electrical and electronic applications at elevated temperatures. Retains good electrical properties at high temperatures. Self-extinguishing. Low dielectric loss factor at high frequencies.Applications: Nozzle insulators in wire welding guns where a shielding gas is used.Information provided by Elektro-Isola

Physical Properties	Metric	English	Comments
Density	1.80 g/cc @Thickness >=0.000 mm	0.0650 lb/in³ @Thickness >=0.000 in	24hr/23°C/50% RH; ISO 1183-A; IEC/EN 61212-2 7.3
Water Absorption	0.020 %	0.020 %	24hr/50°C+24hr in water at 23°C; ISO 62-1; IEC/EN 61212-2 7.2

Mechanical Properties	Metric	English	Comments
Flexural Strength	120 MPa @Diameter >=100 mm	17400 psi @Diameter >=3.94 in	24hr/23°C/50% RH; ISO 178; IEC/EN 61212-2 5.1
Compressive Strength	65.0 MPa @Temperature 23.0 °C, Time 86400 sec	9430 psi @Temperature 73.4 °F, Time 24.0 hour	50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2
Adhesive Bond Strength	150 MPa @Diameter <=100 mm	21800 psi @Diameter <=3.94 in	24hr/23°C/50% RH; IEC 60212-2; IEC/EN 61212-2 5.3

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	210 °C @Thickness 3.00 mm, Time 7.20e+7 sec	410 °F @Thickness 0.118 in, Time 20000 hour	IEC 60695-11-10; IEC/EN 61212-2 7.1
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10; IEC/EN 61212-2 7.4

Electrical Properties	Metric	English	Comments
Insulation Resistance	5.00e+9 ohm @Diameter 8.00 - 10.0 mm	5.00e+9 ohm @Diameter 0.315 - 0.394 in	24hr/50°C+24h in water at 23°C; IEC; IEC/EN 61212-2 6.2
Dielectric Constant	4.0 @Frequency 50.0 Hz	4.0 @Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3
Dielectric Strength	6.70 kV/mm @Thickness 3.00 mm	170 kV/in @Thickness 0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60243-1; IEC/EN 61212-2 6.1.2.1
	1.60 kV/mm @Diameter >=3.00 mm	40.6 kV/in @Diameter >=0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60243-1; IEC/EN 61212-2 6.1.2.1
Dissipation Factor	0.0060 @Frequency 50.0 Hz	0.0060 @Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3
	0.0060 @Frequency 1000 Hz	0.0060 @Frequency 1000 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 250; IEC/EN 61212-2 6.3