Elektro-Isola G-Etronax EP S Epoxy, Glass Fabric Reinforcement, Green, Sheets

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler
Manufacturer Elektro-Isola
Trade Name G-Etronax
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Elektro-Isola G-Etronax EP S Epoxy, Glass Fabric Reinforcement, Green, Sheets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Particularly good electrical and mechanical properties by continuous use, even at high temperatures. Very good chemical resistance. Engineering and insulation material in electrical machinery, transformers and chemical plants. Suitable for mechanical applications. The flexural strength and modulus of elasticity values are measured along the sheet.Applications: Wear parts/vanes in oil-lubricated vacuum pumps.Information provided by Elektro-Isola
Physical Properties Metric English Comments
Density 1.90 g/cc
0.0686 lb/in³
24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption 0.20 %
0.20 %
24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2
Mechanical Properties Metric English Comments
Tensile Strength 320 MPa

@Thickness >=1.50 mm
46400 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity 24.0 GPa

@Thickness >=1.50 mm
3480 ksi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength 375 MPa

@Thickness >=1.50 mm
54400 psi

@Thickness >=0.0591 in
1hr/180°C/measured at 180°C; ISO 178; IEC/EN 60893-2 5.1
500 MPa

@Thickness >=1.50 mm
72500 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Compressive Strength 600 MPa

@Thickness >=5.00 mm
87000 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength 60.0 MPa

@Thickness >=5.00 mm
8700 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO) 80.0 kJ/m²

@Thickness >=5.00 mm
38.1 ft-lb/in²

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 200 °C

@Thickness 0.000 mm,
Time 7.20e+7 sec
392 °F

@Thickness 0.000 in,
Time 20000 hour
IEC 60216; IEC/EN 60893-2 7.1
Electrical Properties Metric English Comments
Insulation Resistance 2.00e+11 ohm

@Thickness >=3.00 mm
2.00e+11 ohm

@Thickness >=0.118 in
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant 5.0

@Thickness <=3.00 mm,
Frequency 50.0 Hz
5.0

@Thickness <=0.118 in,
Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
5.0

@Thickness <=3.00 mm,
Frequency 1.00e+6 Hz
5.0

@Thickness <=0.118 in,
Frequency 1.00e+6 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength 3.20 kV/mm

@Thickness >=3.00 mm
81.3 kV/in

@Thickness >=0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
18.0 kV/mm

@Thickness 3.00 mm
457 kV/in

@Thickness 0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor 0.0080

@Frequency 50.0 Hz
0.0080

@Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index 400 V

@Thickness 3.00 mm
400 V

@Thickness 0.118 in
IEC 60112; IEC/EN 60893-2 6.4