Elektro-Isola G-Etronax EP FR4 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler
Manufacturer Elektro-Isola
Trade Name G-Etronax
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Elektro-Isola G-Etronax EP FR4 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Extremely high mechanical strength at moderate temperature. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. UL-94 V-0 approved – File No. E222199Information provided by Elektro-Isola
Physical Properties Metric English Comments
Density 1.90 g/cc
0.0686 lb/in³
24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption 0.13 %
0.13 %
24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2
Mechanical Properties Metric English Comments
Tensile Strength 320 MPa

@Thickness >=1.50 mm
46400 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity 22.0 GPa

@Thickness >=1.50 mm
3190 ksi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength 200 MPa

@Thickness >=1.50 mm
29000 psi

@Thickness >=0.0591 in
1hr/150°C/measured at 150°C; ISO 178; IEC/EN 60893-2 5.1
450 MPa

@Thickness >=1.50 mm
65300 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
70.0 MPa

@Treatment Temp. 200 °C,
Time 3600 sec
10200 psi

@Treatment Temp. 392 °F,
Time 1.00 hour
ISO 178; IEC/EN 60893-2 5.1
220 MPa

@Treatment Temp. 150 °C,
Time 3600 sec
31900 psi

@Treatment Temp. 302 °F,
Time 1.00 hour
ISO 178; IEC/EN 60893-2 5.1
280 MPa

@Treatment Temp. 100 °C,
Time 3600 sec
40600 psi

@Treatment Temp. 212 °F,
Time 1.00 hour
ISO 178; IEC/EN 60893-2 5.1
420 MPa

@Treatment Temp. 50.0 °C,
Time 3600 sec
60900 psi

@Treatment Temp. 122 °F,
Time 1.00 hour
ISO 178; IEC/EN 60893-2 5.1
470 MPa

@Treatment Temp. 20.0 °C,
Time 3600 sec
68200 psi

@Treatment Temp. 68.0 °F,
Time 1.00 hour
ISO 178; IEC/EN 60893-2 5.1
Compressive Strength 550 MPa

@Thickness >=5.00 mm
79800 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength 55.0 MPa

@Thickness >=5.00 mm
7980 psi

@Thickness >=0.197 in
24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO) 65.0 kJ/m²

@Thickness >=5.00 mm
30.9 ft-lb/in²

@Thickness >=0.197 in
24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 145 °C

@Thickness 0.000 mm,
Time 7.20e+7 sec
293 °F

@Thickness 0.000 in,
Time 20000 hour
IEC 60216; IEC/EN 60893-2 7.1
Flammability, UL94 V-0
V-0
IEC/EN 60893-2 7.2; IEC 60695-11-10
Electrical Properties Metric English Comments
Insulation Resistance 5.00e+11 ohm

@Thickness >=3.00 mm
5.00e+11 ohm

@Thickness >=0.118 in
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant 4.5

@Thickness <=3.00 mm,
Frequency 50.0 Hz
4.5

@Thickness <=0.118 in,
Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
4.5

@Thickness <=3.00 mm,
Frequency 1.00e+6 Hz
4.5

@Thickness <=0.118 in,
Frequency 1.00e+6 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength 2.80 kV/mm

@Thickness >=3.00 mm
71.1 kV/in

@Thickness >=0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
15.0 kV/mm

@Thickness 3.00 mm
381 kV/in

@Thickness 0.118 in
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor 0.0050

@Frequency 50.0 Hz
0.0050

@Frequency 50.0 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
0.0080

@Frequency 1.00e+6 Hz
0.0080

@Frequency 1.00e+6 Hz
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index 200 V

@Thickness 3.00 mm
200 V

@Thickness 0.118 in
IEC 60112; IEC/EN 60893-2 6.4