Ecomass® 1080CO94 Copper Powder Filled Polyamide Alloy, Injection Molding

Category Polymer , Thermoplastic , Nylon
Manufacturer Ecomass Technologies
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ecomass® 1080CO94 Copper Powder Filled Polyamide Alloy, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Moderate Specific Gravity, Copper Powder Filled Polyamide (PA) Alloy, Good Toughness, Product Form - PelletsProcessing Method: Injection MoldingNontoxic alternative to Lead, weighting and balancing applicationsInformation provided by Technical Polymers.
Physical Properties Metric English Comments
Specific Gravity 6.00 g/cc
6.00 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 31.7 MPa
4600 psi
ASTM D638
Elongation at Break 8.0 %
8.0 %
ASTM D638
Tensile Modulus 9.10 GPa
1320 ksi
ASTM D638
Flexural Strength 46.9 MPa
6800 psi
ASTM D790
Flexural Modulus 5.24 GPa
760 ksi
ASTM D790
Izod Impact, Notched 0.801 J/cm
1.50 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 204 - 254 °C
400 - 490 °F
Mold Temperature 57.2 - 82.2 °C
135 - 180 °F
Drying Temperature 73.9 °C
165 °F
Dry Time 4 hour
4 hour