Eastman Tritan TX1501HF Copolyester
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | Eastman Chemical |
| Trade Name | Tritan |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tritan TX1501HF Copolyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eastman Tritan TX1501HF is a high flow grade of Eastman Tritan. Eastman Tritan TX1501HF has viscosity reductions of 40-50% relative to Eastman Tritan copolyester TX1001. Eastman Tritan copolyester TX1501HF contains a mold release derived from vegetable based sources. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance.Application/UsesAppliancesConsumer goodsDurable goodsHousewaresKey AttributesEase of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceGood flowabilityGood heat resistanceOutstanding impact resistanceQuick cycle timesTypical properties as listed are from preliminary data. Information was provided by Eastman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 210 % | 210 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.575 GPa | 228.4 ksi | ASTM D638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | ASTM D790 |
| Flexural Modulus | 1.575 GPa | 228.4 ksi | ASTM D790 |
| Izod Impact, Notched | 8.60 J/cm | 16.1 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D1003 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes | Repeated use food contact articles |
| NSF | Yes | Yes | Food equipment materials & Drinking water system components - health effects; NSF/ANSI Standards 51 & 61 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 282 °C | 500 - 540 °F | |
| Mold Temperature | 38.0 - 66.0 °C | 100 - 151 °F | |
| Drying Temperature | 88.0 °C | 190 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- Parabeam Industrie Paraglass 12 3D Glass Fabric
- Advanced Elastomer Systems Trefsin® 3101-75 W305 Thermoplastic Rubber (discontinued **)
- Premix Thermoplastics PREADD PA 143 (discontinued **)
- Karina 806-48/1-H-ISE-LMP Black PVC Compound
- Universal Wire Works E91T1-B3 Flux Cored Carbon Steel Tubular Electrode
- Polyplastics Duracon® SX-35 Acetal Co-polymer (POM), Flexible, Lower noise
- Covestro Makrolon® 1881 Polycarbonate
- CP-Polymer-Technik Wellamid® 6600 GV 30 HWCP 30% Glass Fiber Nylon 66, Heat Stabilized, Conditioned
- E-Polymers TEKAMID® H14ST Super Toughness PA/ABS Alloy
- E-Polymers TEKAFIN® PH50GM 30% Glass Fiber Reinforced Mineral Filled Low Warpage Compounded-PP
Copyright © lookpolymers.com All Rights Reserved