Eastman Tritan MP100 Copolyester

Category Polymer , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer Eastman Chemical
Trade Name Tritan
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tritan MP100 Copolyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eastman Tritan MP100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan MP100 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is not suitable for autoclave/steam sterilization. Eastman Tritan MP100 has been formulated for use in medical film, sheet, and packaging applications.Application/UsesDevice packagingExtruded medical films and sheetingMedical articles from sheetRigid medical packagingSterile medical packagingKey AttributesGood toughnessDoes not contain Bisphenol-A (BPA)Does not contain plasticizersEnduring sustainabilityExcellent heat resistanceOutstanding chemical resistanceReliable, predictable processing for extrusion, thermoforming, heat and radio frequency sealingSuitable for most forms of sterilizationGood, long-term clarityInformation was provided by Eastman.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ASTM D1505
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
ASTM D570
Water Vapor Transmission 4.00 g/m²/day

@Temperature 23.0 °C
0.258 g/100 in²/day

@Temperature 73.4 °F
ASTM F1249
11.0 g/m²/day

@Temperature 38.0 °C
0.708 g/100 in²/day

@Temperature 100 °F
ASTM F1249
Oxygen Transmission 32.0 cc-mm/m²-24hr-atm
81.3 cc-mil/100 in²-24hr-atm
ASTM D3985
Carbon Dioxide Transmission 149 cc-mm/m²-24hr-atm
378 cc-mil/100 in²-24hr-atm
ASTM D1434
Thickness 250 microns
9.84 mil
Thickness of film tested; ASTM D374
Surface Tension 45 dynes/cm
45 dynes/cm
Polar; ASTM D5946
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 41.0 MPa
5950 psi
ASTM D882
Film Tensile Strength at Yield, TD 40.0 MPa
5800 psi
ASTM D882
Film Elongation at Break, MD 179 %
179 %
ASTM D882
Film Elongation at Break, TD 203 %
203 %
ASTM D882
Film Elongation at Yield, MD 7.0 %
7.0 %
ASTM D882
Film Elongation at Yield, TD 7.0 %
7.0 %
ASTM D882
Secant Modulus, MD 1.462 GPa
212.0 ksi
ASTM D882
Secant Modulus, TD 1.383 GPa
200.6 ksi
ASTM D882
Puncture Energy 4.60 J

@Temperature 23.0 °C
3.39 ft-lb

@Temperature 73.4 °F
Dynatup; ASTM D3763
Tear Strength 11.0 kN/m
62.8 pli
MD; Trouser @200/mm/min; ISO 6383-1
11.0 kN/m
62.8 pli
TD; Trouser @200/mm/min; ISO 6383-1
12.0 kN/m
68.5 pli
Split tear method, TD; ASTM D1938
13.0 kN/m
74.2 pli
Split tear method, MD; ASTM D1938
Elmendorf Tear Strength MD 509 g
509 g
ASTM D1922
Elmendorf Tear Strength TD 612 g
612 g
ASTM D1922
Elmendorf Tear Strength, MD 2.00 g/micron
50.8 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.40 g/micron
61.0 g/mil
ASTM D1922
Dart Drop 3.47 g/micron

@Temperature -18.0 °C
88.1 g/mil

@Temperature -0.400 °F
ASTM 1709A
3.53 g/micron

@Temperature 23.0 °C
89.7 g/mil

@Temperature 73.4 °F
ASTM 1709A
3.65 g/micron

@Temperature -30.0 °C
92.7 g/mil

@Temperature -22.0 °F
ASTM 1709A
Dart Drop Test 867 g

@Temperature -18.0 °C
1.91 lb

@Temperature -0.400 °F
ASTM 1709A
882 g

@Temperature 23.0 °C
1.94 lb

@Temperature 73.4 °F
ASTM 1709A
913 g

@Temperature -30.0 °C
2.01 lb

@Temperature -22.0 °F
ASTM 1709A
Film Tensile Strength at Break, MD 59.0 MPa
8560 psi
ASTM D882
Film Tensile Strength at Break, TD 52.0 MPa
7540 psi
ASTM D882
Thermal Properties Metric English Comments
CTE, linear 88.0 µm/m-°C
48.9 µin/in-°F
ASTM D696
Specific Heat Capacity 1.72 J/g-°C

@Temperature 60.0 °C
0.410 BTU/lb-°F

@Temperature 140 °F
DSC
1.88 J/g-°C

@Temperature 100 °C
0.450 BTU/lb-°F

@Temperature 212 °F
DSC
2.26 J/g-°C

@Temperature 150 °C
0.540 BTU/lb-°F

@Temperature 302 °F
DSC
2.43 J/g-°C

@Temperature 200 °C
0.580 BTU/lb-°F

@Temperature 392 °F
DSC
2.59 J/g-°C

@Temperature 250 °C
0.620 BTU/lb-°F

@Temperature 482 °F
DSC
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
ASTM D1790
Glass Transition Temp, Tg 110 °C
230 °F
DSC
Optical Properties Metric English Comments
Refractive Index 1.545
1.545
ASTM D542
Haze 1.0 %
1.0 %
ASTM D1003
Gloss 161 %
161 %
@ 60°; ASTM D2457
Transmission, Visible 92 %
92 %
ASTM D1003
UV Transmittance 89 %

@Thickness 0.380 mm
89 %

@Thickness 0.0150 in
UV/Vis Spectro
Descriptive Properties Value Comments
PPT Tear Resistance, M.D. 42 N
ASTM D2582
PPT Tear Resistance, T.D. 56 N
ASTM D2582
Taber Abrasion 23% haze
ASTM 1044, Average at 25 cycles