Eastman Tenite 383A-12 CAP Cellulose Acetate Propionate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 383A-12 CAP Cellulose Acetate Propionate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min |
| Elongation at Break | 37 % | 37 % | |
| Elongation at Yield | 3.9 % | 3.9 % | |
| Tensile Modulus | 1.46 GPa | 212 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.98 J/cm² | 9.42 ft-lb/in² | |
| 1.04 J/cm² @Temperature -30.0 °C |
4.95 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 107 µm/m-°C @Temperature 20.0 °C |
59.4 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 134 µm/m-°C @Temperature 20.0 °C |
74.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | |
| Vicat Softening Point | 89.0 °C | 192 °F | |
| Glass Transition Temp, Tg | 100 °C | 212 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 225 - 240 °C | 437 - 464 °F |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1033TL Nylon 6/6 (DAM) (discontinued **)
- Lucent Polymers GPP-120 Polypropylene Homopolymer, 20% Glass Fiber Reinforced, Chemically Coupled
- SABIC Innovative Plastics LNP LUBRICOMP OX97635 PPS
- Dow Corning SE 4430 KIT
- CP-Polymer-Technik Wellamid® 6000 GS 30 HWCP 30% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- 3M 12050 Black 1/2" (12.7 mm) Polyurethane Foam
- Braskem GM5010T2 HDPE High Density Extrusion Polyethylene
- Aclo Accutech Polypropylene Homopolymer HP0334W30L1 Wollastonite Reinforced
- Bulk Molding Compounds BMC T40(20) Die Casting Replacement Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved