Eastman Tenite 371A-12 CAP Cellulose Acetate Propionate  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 371A-12 CAP Cellulose Acetate Propionate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0060 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min
Elongation at Break 42 %
42 %
Elongation at Yield 3.8 %
3.8 %
Tensile Modulus 1.59 GPa
231 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Charpy Impact, Notched 2.17 J/cm²
10.3 ft-lb/in²
1.05 J/cm²

@Temperature -30.0 °C
5.00 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 131 µm/m-°C

@Temperature 20.0 °C
72.8 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 91.0 °C
196 °F
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C
181 °F
Vicat Softening Point 88.0 °C
190 °F
Glass Transition Temp, Tg 101 °C
214 °F
Processing Properties Metric English Comments
Melt Temperature 220 - 230 °C
428 - 446 °F