Eastman Tenite 130-33 Cellulose Acetate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 130-33 Cellulose Acetate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
33% Plasticized, contains 100% fiber grade ester.ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min |
| Elongation at Break | 18 % | 18 % | |
| Elongation at Yield | 3.1 % | 3.1 % | |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.63 J/cm² | 7.76 ft-lb/in² | |
| 0.520 J/cm² @Temperature -30.0 °C |
2.47 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 127 µm/m-°C @Temperature 20.0 °C |
70.6 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 151 µm/m-°C @Temperature 20.0 °C |
83.9 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 78.0 °C | 172 °F | |
| Glass Transition Temp, Tg | 100 °C | 212 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 220 °C | 401 - 428 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® MC1300 PC+ABS (Asia Pacific)
- SABIC Innovative Plastics Lexan® ML4506 PC
- Solvay Specialty Polymers Torlon® 4000TF Polyamide-imide (PAI) (Unverified Data**)
- Shuman FR380 Grey PC/ABS Alloy, Flame Retardant
- Styron Magnumâ„¢ 4455 ABS
- A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
- Epoxy Technology EPO-TEK® OG133-8 UV Cure Optical Epoxy
- Eurofoam Gummicell GU 250 0,70 NR Foam
- 3M FP532 Clear Polypropylene Label Products
- BASF Pluracol® GP 430R Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved