Eastman Tenite 105-33 Cellulose Acetate  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 105-33 Cellulose Acetate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
33% Plasticized ISO data as provided by the manufacturer, Eastman Chemical.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0060 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 29.0 MPa
4210 psi
50 mm/min
Elongation at Break 19 %
19 %
Elongation at Yield 3.3 %
3.3 %
Tensile Modulus 1.62 GPa
235 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
Charpy Impact, Notched 1.59 J/cm²
7.57 ft-lb/in²
0.490 J/cm²

@Temperature -30.0 °C
 2.33 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 106 µm/m-°C

@Temperature 20.0 °C
 58.9 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 146 µm/m-°C

@Temperature 20.0 °C
 81.1 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 86.0 °C
187 °F
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Vicat Softening Point 80.0 °C
176 °F
Glass Transition Temp, Tg 96.0 °C
205 °F
Processing Properties Metric English Comments
Melt Temperature 205 - 220 °C
401 - 428 °F