Eastman Embrace HY1000 Copolyester for Shrink Film

Category Polymer , Film , Thermoplastic , Polyester, TP
Manufacturer Eastman Chemical
Trade Name Embrace
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Embrace HY1000 Copolyester for Shrink Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications:Beverage packagingCosmetics/personal care packagingDairy packagingFood packagingJuice packagingPharmaceutical packagingKey Attributes:Eye catching 360° graphic capabilityNoise-free shrink film density less than 1.0g/ccSoft touch for easy gripUltimate shrinkage of 70%UV protectionProduct Description: Eastman Embrace HY1000 compound is combined with Eastman Embrace copolyester to create a white opaque microvoided shrinkable film. Eastman Embrace HY copolyester can have a density below 1.0 g/cc with a high ultimate shrinkage of up to 70%. Benefits of Eastman Embrace HY copolyester such as UV protection, low density for recycling needs and a soft hand for squeeze applications offer a robust packaging solution that is appealing to the consumer and functionable for the brand owner. This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.Information provided by Eastman.
Physical Properties Metric English Comments
Density 0.890 g/cc
0.0322 lb/in³
ASTM D1505
Water Vapor Transmission 38.2 g/m²/day
2.46 g/100 in²/day
ASTM F1249
Oxygen Transmission 10.4 cc-mm/m²-24hr-atm

@Temperature 30.0 °C
26.4 cc-mil/100 in²-24hr-atm

@Temperature 86.0 °F
ASTM D3985
Carbon Dioxide Transmission 42.7 cc-mm/m²-24hr-atm

@Temperature 30.0 °C
108 cc-mil/100 in²-24hr-atm

@Temperature 86.0 °F
ASTM D1434
Thickness 63.5 microns
2.50 mil
Surface Tension 36.3 dynes/cm
36.3 dynes/cm
Harmonic Mean - Dispersive
36.3 dynes/cm
36.3 dynes/cm
Harmonic Mean - Total
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 380 %
380 %
ASTM D882
Film Elongation at Break, TD 22 %
22 %
ASTM D882
Tensile Modulus 0.850 GPa
123 ksi
Film M.D.; ASTM D882
3.00 GPa
435 ksi
Film T.D.; ASTM D882
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 117 MPa
17000 psi
ASTM D882
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 77.0 °C
171 °F
Internal Method
Shrinkage, MD -1.00 %

@Temperature 95.0 °C,
Time 10.0 sec
-1.00 %

@Temperature 203 °F,
Time 0.00278 hour
Shrinkage, TD 73 %

@Temperature 95.0 °C,
Time 10.0 sec
73 %

@Temperature 203 °F,
Time 0.00278 hour
Optical Properties Metric English Comments
Gloss 8.0 %
8.0 %
at 60°; ASTM D2457
Yellow Index 1.71 %
1.71 %
ASTM E313
UV Transmittance 0.20 %

@Thickness 0.300 mm
0.20 %

@Thickness 0.0118 in
6.0 %

@Thickness 0.325 mm
6.0 %

@Thickness 0.0128 in
9.8 %

@Thickness 0.350 mm
9.8 %

@Thickness 0.0138 in
11.5 %

@Thickness 0.375 mm
11.5 %

@Thickness 0.0148 in
12.5 %

@Thickness 0.400 mm
12.5 %

@Thickness 0.0157 in
Descriptive Properties Value Comments
Color -0.026
b*
-0.17
a*
91.4
Opacity
93.4
L*, ASTM E1331