Eastman D4036-F Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman D4036-F Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
D4036-F is a low density formulation with high slip and high antiblock. It is suggested for film applications requiring a good balance of properties, such as converter film for industrial and general-purpose packagingList of Applications: FilmsPackagingD4036-F meets the requirements of FDA regulations at 21 CFR 177.1520(c)(2.2) and may be used as a component of packages used for holding food during cooking. However, the polymer thickness in the form in which it contacts food shall not exceed 0.005 inches and contact is limited to non-alcoholic food because of a regulatory limitation for an adjuvant substance in this formulation.Information supplied by the manufacturer.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D4883
Moisture Vapor Transmission 18.6 cc-mm/m²-24hr-atm
47.2 cc-mil/100 in²-24hr-atm
ASTM F372
Oxygen Transmission 200 cc-mm/m²-24hr-atm
508 cc-mil/100 in²-24hr-atm
ASTM D1434
Thickness 32.0 microns
1.26 mil
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 26.0 MPa
3770 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 250 %
250 %
ASTM D882
Film Elongation at Break, TD 750 %
750 %
ASTM D882
Secant Modulus, MD 0.186 GPa
27.0 ksi
1% Secant; ASTM D882
Secant Modulus, TD 0.220 GPa
31.9 ksi
1% Secant; ASTM D882
Coefficient of Friction <= 0.10
<= 0.10
ASTM D1894
Elmendorf Tear Strength MD 400 g
400 g
Elmendorf Tear Strength TD 140 g
140 g
Elmendorf Tear Strength, MD 12.5 g/micron
318 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.40 g/micron
112 g/mil
ASTM D1922
Dart Drop 3.10 g/micron
78.7 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 26.0 MPa
3770 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 94.0 °C
201 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 11 %
11 %
ASTM D1003
Gloss 55 %
55 %
at 45°; ASTM D2457
Transmission, Visible 80 %
80 %
ASTM D1746