Eastman Cadence™ GS4 Copolyester for film calendering

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer Eastman Chemical
Trade Name Cadence™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Cadence™ GS4 Copolyester for film calendering.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in different grades, it features ease of processing, high-melt strength, aesthetics, clarity and gloss.BenefitsCan be used on existing calendering lines with no or minimal modification.No drying is needed prior to the calendering process.Good thermal stability during normal calendering process conditions.No corrosive degradation products are normally formed.Easy to emboss for added texture and dimensions with standard engraved rolls. Easy to decorate using offset lithography, flexographic, and screen-printing processes.Thermoforms easily and is compatible with commercial adhesives used in lamination processesEnvironmentally responsible material.Product description: Eastman Cadence GS5 is an amorphous copolyester with improved processability for film calendering. Calendered films made of Eastman Cadence copolyesters are non-crystallizing, are halogen-free, offer wide calendering and thermoforming windows and have good low-temperature toughness. They are cooperative in secondary operations such as solvent-bonding, lamination, decoration, cold-forming, punching/cutting and embossment.Eastman Cadence resins require no pre-drying or additional stabilizers.Application/UsesAppliance filmsArchitectural laminatesAutomotive filmsBagsDecorative laminatesElectronic laminatesFloor coveringsFurniture/Furniture trimLabelsOutdoor filmsPackagingPrintable filmsShrink filmTransaction cardsTransportation laminatesWall coveringsReported typical properties are preliminary. Information was provided by Eastman.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ASTM D1505
Water Absorption 0.15 %

@Time 86400 sec
0.15 %

@Time 24.0 hour
Immersion; ASTM D570
Thermal Properties Metric English Comments
CTE, linear 76.1 µm/m-°C

@Temperature -30.0 - 30.0 °C
42.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Specific Heat Capacity 1.30 J/g-°C

@Temperature 60.0 °C
0.310 BTU/lb-°F

@Temperature 140 °F
DSC
1.72 J/g-°C

@Temperature 100 °C
0.410 BTU/lb-°F

@Temperature 212 °F
DSC
1.84 J/g-°C

@Temperature 150 °C
0.440 BTU/lb-°F

@Temperature 302 °F
DSC
1.97 J/g-°C

@Temperature 200 °C
0.470 BTU/lb-°F

@Temperature 392 °F
DSC
2.05 J/g-°C

@Temperature 250 °C
0.490 BTU/lb-°F

@Temperature 482 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 68.0 °C
154 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
ASTM D648
Vicat Softening Point 79.0 °C
174 °F
ASTM D1525
Glass Transition Temp, Tg 80.0 °C
176 °F
DSC
Oxygen Index 24.7 %
24.7 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 4.55e+16 ohm-cm
4.55e+16 ohm-cm
ASTM D257
Surface Resistivity per Square 1.99e+16 ohm
1.99e+16 ohm
ASTM D257
Dielectric Constant 2.95

@Frequency 1.00e+6 Hz
2.95

@Frequency 1.00e+6 Hz
ASTM D150
3.2

@Frequency 1000 Hz
3.2

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 15.5 kV/mm
394 kV/in
Short time, 500 V/sec rate-of-rise; ASTM D149
Dissipation Factor 0.017

@Frequency 1000 Hz
0.017

@Frequency 1000 Hz
ASTM D150
0.022

@Frequency 1.00e+6 Hz
0.022

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 134 sec
134 sec
ASTM D495
Descriptive Properties Value Comments