Eastman 1550F Film Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman 1550F Film Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyethylene 1550F is a low density polyethylene that contains no additives.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Base Resin Density 0.918 g/cc
0.0332 lb/in³
ASTM D4883
Water Vapor Transmission 18.6 g/m²/day
1.20 g/100 in²/day
ASTM F372
Oxygen Transmission 200 cc-mm/m²-24hr-atm
508 cc-mil/100 in²-24hr-atm
ASTM D3985
Thickness 38.0 microns
1.50 mil
Base Resin Melt Index 3.5 g/10 min
3.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 29.0 MPa
4210 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ASTM D882
Film Elongation at Break, MD 200 %
200 %
ASTM D882
Film Elongation at Break, TD 650 %
650 %
ASTM D882
Secant Modulus, MD 0.193 GPa
28.0 ksi
0.01; ASTM D882
Secant Modulus, TD 0.227 GPa
32.9 ksi
0.01; ASTM D882
Coefficient of Friction 0.70
0.70
ASTM D1894
Elmendorf Tear Strength, MD 9.21 g/micron
234 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 1.84 g/micron
46.7 g/mil
ASTM D1922
Dart Drop 2.63 g/micron
66.8 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
ASTM D882
Film Tensile Strength at Break, TD 16.0 MPa
2320 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 89.0 °C
192 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 20 %
20 %
ASTM D1003
Gloss 30 %
30 %
at 45°; ASTM D2457
Transmission, Visible 70 %
70 %
Transparency; ASTM D1746
Descriptive Properties Value Comments
Process Film