EVALCA EVAL® LC-T101 Ethylene Vinyl Alcohol Copolymer Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Alcohol (EVOH)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EVALCA EVAL® LC-T101 Ethylene Vinyl Alcohol Copolymer Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
32 mol % Ethylene.Data provided by EVALCA. Applications: Solid phase pressure forming. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D1505
Moisture Vapor Transmission 1.50 cc-mm/m²-24hr-atm
3.81 cc-mil/100 in²-24hr-atm
40°C, 90% RH
Oxygen Transmission 0.0100 cc-mm/m²-24hr-atm
0.0254 cc-mil/100 in²-24hr-atm
20°C; 65% RH; Permeability increases significantly at higher moisture content.
Melt Flow 1.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
4.4 g/10 min

@Load 2.16 kg,
Temperature 210 °C
4.4 g/10 min

@Load 4.76 lb,
Temperature 410 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
Tensile Strength, Yield 71.0 MPa
10300 psi
10%/min. ASTM D638
Film Elongation at Break, MD 270 %
270 %
Orientation not specified; ASTM D882
Modulus of Elasticity 1.90 GPa
276 ksi
Youngs Modulus, ASTM D638, 10%/min.
Film Tensile Strength at Break, MD 65.0 MPa
9430 psi
Orientation not specified; ASTM D882
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C
33.3 µin/in-°F
Below Tg
120 µm/m-°C
66.7 µin/in-°F
Above Tg
Specific Heat Capacity 2.40 J/g-°C
0.574 BTU/lb-°F
Estimated by MatWeb from similar grades
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
For EVAL F101
Melting Point 183 °C
361 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
For EP-F101
Vicat Softening Point 173 °C
343 °F
For EP-F101
Glass Transition Temp, Tg 69.0 °C
156 °F
Dynamic Viscoelasticity
Optical Properties Metric English Comments
Haze 1.9 %
1.9 %
Film; ASTM D1003
Gloss 85 %
85 %
45°; Film; ASTM D2457
Electrical Properties Metric English Comments
Dielectric Constant 5.5
5.5
Frequency Not Specified
Dissipation Factor 0.21
0.21
Frequency Not Specified
Processing Properties Metric English Comments
Melt Temperature <= 240 °C
<= 464 °F