EVALCA EVAL® LC-H101BD Ethylene Vinyl Alcohol Copolymer Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Alcohol (EVOH)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EVALCA EVAL® LC-H101BD Ethylene Vinyl Alcohol Copolymer Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
38 mol % Ethylene.Data provided by EVALCA. Applications: Blown film. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D1505
Moisture Vapor Transmission 0.820 cc-mm/m²-24hr-atm
2.08 cc-mil/100 in²-24hr-atm
40°C, 90% RH
Oxygen Transmission 0.0140 cc-mm/m²-24hr-atm
0.0356 cc-mil/100 in²-24hr-atm
20°C; 65% RH; Permeability increases significantly at higher moisture content.
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
3.8 g/10 min

@Load 2.16 kg,
Temperature 210 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 410 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
Tensile Strength, Yield 67.0 MPa
9720 psi
10%/min. ASTM D638
Film Elongation at Break, MD 250 %
250 %
Orientation not specified; ASTM D882
Elongation at Yield 6.0 %
6.0 %
10%/min. ASTM D638
Modulus of Elasticity 2.40 GPa
348 ksi
Youngs Modulus, ASTM D638, 10%/min.
Flexural Yield Strength 108 MPa
15700 psi
Bending Strength; ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
Bending Elasticity; ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Taber Abrasion, mg/1000 Cycles 2.0
2.0
ASTM D1175
Film Tensile Strength at Break, MD 59.0 MPa
8560 psi
Orientation not specified; ASTM D882
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C
38.9 µin/in-°F
Below Tg
120 µm/m-°C
66.7 µin/in-°F
Above Tg
Specific Heat Capacity 2.40 J/g-°C
0.574 BTU/lb-°F
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
For EVAL F101
Melting Point 175 °C
347 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Vicat Softening Point 165 °C
329 °F
Glass Transition Temp, Tg 62.0 °C
144 °F
Dynamic Viscoelasticity
Optical Properties Metric English Comments
Haze 1.5 %
1.5 %
Film; ASTM D1003
Gloss 90 %
90 %
45°; Film; ASTM D2457
Electrical Properties Metric English Comments
Dielectric Constant 5.4
5.4
Frequency Not Specified
Dissipation Factor 0.22
0.22
Frequency Not Specified
Processing Properties Metric English Comments
Melt Temperature <= 240 °C
<= 464 °F