EVALCA EVAL® LC-E151B Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Alcohol (EVOH) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EVALCA EVAL® LC-E151B Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
44 mol % Ethylene.Data provided by EVALCA. Applications: Melt phase forming, solid phase pressure forming, blow molding, tubes EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D1505 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | Equilibrium at 50% RH |
| 1.5 % | 1.5 % | 50% RH | |
| Water Absorption at Saturation | 5.0 % | 5.0 % | 100% RH |
| Moisture Vapor Transmission | 0.540 cc-mm/m²-24hr-atm | 1.37 cc-mil/100 in²-24hr-atm | 40°C, 90% RH |
| Oxygen Transmission | 0.0300 cc-mm/m²-24hr-atm | 0.0762 cc-mil/100 in²-24hr-atm | 20°C; 65% RH; Permeability increases significantly at higher moisture content. |
| Melt Flow | 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| 3.5 g/10 min @Load 2.16 kg, Temperature 210 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | 10%/min. ASTM D638 |
| Film Elongation at Break, MD | 280 % | 280 % | Orientation not specified; ASTM D882 |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | Youngs Modulus, ASTM D638, 10%/min. |
| Film Tensile Strength at Break, MD | 51.0 MPa | 7400 psi | Orientation not specified; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | Below Tg |
| 130 µm/m-°C | 72.2 µin/in-°F | Above Tg | |
| Specific Heat Capacity | 2.40 J/g-°C | 0.574 BTU/lb-°F | |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | For EVAL F101 |
| Melting Point | 165 °C | 329 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | For EP-E105 |
| Vicat Softening Point | 155 °C | 311 °F | For EP-E105 |
| Glass Transition Temp, Tg | 55.0 °C | 131 °F | Dynamic Viscoelasticity |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % | 1.7 % | Film; ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; Film; ASTM D2457 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.20e+13 ohm-cm | 1.20e+13 ohm-cm | |
| Surface Resistance | 2.10e+15 ohm | 2.10e+15 ohm | |
| Dielectric Constant | 5.0 | 5.0 | Frequency Not Specified |
| Dissipation Factor | 0.22 | 0.22 | Frequency Not Specified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 250 °C | <= 482 °F |