EVALCA EVAL® G156A Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Alcohol (EVOH)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EVALCA EVAL® G156A Ethylene Vinyl Alcohol Copolymer Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

48 mol % Ethylene.Data provided by EVALCA. Applications: Cast film, specialty applications. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³	ASTM D1505
Moisture Vapor Transmission	0.540 cc-mm/m²-24hr-atm	1.37 cc-mil/100 in²-24hr-atm	40°C, 90% RH
Oxygen Transmission	0.0640 cc-mm/m²-24hr-atm	0.163 cc-mil/100 in²-24hr-atm	20°C; 65% RH; Permeability increases significantly at higher moisture content.
Melt Flow	6.4 g/10 min @Load 2.16 kg, Temperature 190 °C	6.4 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	14.7 g/10 min @Load 2.16 kg, Temperature 210 °C	14.7 g/10 min @Load 4.76 lb, Temperature 410 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	85	85	ASTM D785
Tensile Strength, Yield	43.0 MPa	6240 psi	10%/min. ASTM D638
Film Elongation at Break, MD	330 %	330 %	Orientation not specified; ASTM D882
Modulus of Elasticity	1.90 GPa	276 ksi	Youngs Modulus, ASTM D638, 10%/min.
Film Tensile Strength at Break, MD	37.0 MPa	5370 psi	Orientation not specified; ASTM D882

Thermal Properties	Metric	English	Comments
CTE, linear	100 µm/m-°C	55.6 µin/in-°F	Below Tg
	130 µm/m-°C	72.2 µin/in-°F	Above Tg
Specific Heat Capacity	2.40 J/g-°C	0.574 BTU/lb-°F
Thermal Conductivity	0.340 W/m-K	2.36 BTU-in/hr-ft²-°F	For EVAL F101
Melting Point	158 °C	316 °F	DSC
Deflection Temperature at 0.46 MPa (66 psi)	80.0 °C	176 °F	For EP-E105
Vicat Softening Point	155 °C	311 °F	For EP-E105
Glass Transition Temp, Tg	49.0 °C	120 °F	Dynamic Viscoelasticity

Optical Properties	Metric	English	Comments
Haze	1.9 %	1.9 %	Film; ASTM D1003
Gloss	85 %	85 %	45°; Film; ASTM D2457

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.8	4.8	Frequency Not Specified
Dissipation Factor	0.22	0.22	Frequency Not Specified

Processing Properties	Metric	English	Comments
Melt Temperature	<= 250 °C	<= 482 °F

Users viewing this material also viewed the following: