EVALCA EVAL® G110 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
| Category | Polymer , Thermoplastic , Ethylene Vinyl Alcohol (EVOH) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EVALCA EVAL® G110 Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
48 mol % Ethylene.Data provided by EVALCA. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 0.540 cc-mm/m²-24hr-atm | 1.37 cc-mil/100 in²-24hr-atm | 40°C, 90% RH |
| Oxygen Transmission | 0.0640 cc-mm/m²-24hr-atm | 0.163 cc-mil/100 in²-24hr-atm | 20°C; 65% RH; Permeability increases significantly at higher moisture content. |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C |
15 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | Estimated by MatWeb from similar grades |
| Tensile Strength, Ultimate | 37.0 MPa | 5370 psi | 10%/min; ASTM D638 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 10%/min. ASTM D638 |
| Elongation at Break | 330 % | 330 % | 10%/min. ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | 10%/min. ASTM D638 |
| Modulus of Elasticity | 2.40 GPa | 348 ksi | Youngs Modulus, ASTM D638, 10%/min. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | Below Tg |
| 130 µm/m-°C | 72.2 µin/in-°F | Above Tg | |
| Specific Heat Capacity | 2.40 J/g-°C | 0.574 BTU/lb-°F | Estimated by MatWeb from similar grades |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | For EVAL F101 |
| Melting Point | 156 °C | 313 °F | DSC |
| Vicat Softening Point | 155 °C | 311 °F | For EP-E105 |
| Glass Transition Temp, Tg | 48.0 °C | 118 °F | Dynamic Viscoelasticity |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.9 % | 1.9 % | Estimated by MatWeb from similar grades |
| Gloss | 85 % | 85 % | Estimated by MatWeb from similar grades |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.8 | 4.8 | Frequency Not Specified |
| Dissipation Factor | 0.22 | 0.22 | Frequency Not Specified |