EVALCA EVAL® EP-J102B Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Alcohol (EVOH) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EVALCA EVAL® EP-J102B Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
32 mol % Ethylene.Data provided by EVALCA. Designed to provide a wide thermoforming range together with high barrier properties. EVAL® EP-J102B is specifically designed for thermoforming applications using polystyrene and polyethylene structural layers. This resin can be used with SPPF or melt phase forming techniques. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D1505 |
| Moisture Vapor Transmission | 1.50 cc-mm/m²-24hr-atm | 3.81 cc-mil/100 in²-24hr-atm | 40°C, 90% RH |
| Oxygen Transmission | 0.0120 cc-mm/m²-24hr-atm | 0.0305 cc-mil/100 in²-24hr-atm | 20°C; 65% RH; Permeability increases significantly at higher moisture content. |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| 4.9 g/10 min @Load 2.16 kg, Temperature 210 °C |
4.9 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | Estimated by MatWeb from similar grades |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | Estimated by MatWeb from similar grades |
| Film Elongation at Break, MD | 270 % | 270 % | Orientation not specified; ASTM D882 |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | Estimated by MatWeb from similar grades |
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | Orientation not specified; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
Estimated by MatWeb from similar grades |
| 120 µm/m-°C @Temperature 100 °C |
66.7 µin/in-°F @Temperature 212 °F |
Estimated by MatWeb from similar grades | |
| Specific Heat Capacity | 2.40 J/g-°C | 0.574 BTU/lb-°F | Estimated by MatWeb from similar grades |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | For EVAL F101 |
| Melting Point | 183 °C | 361 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | For EP-H101 |
| Vicat Softening Point | 165 °C | 329 °F | For EP-H101 |
| Glass Transition Temp, Tg | 69.0 °C | 156 °F | Dynamic Viscoelasticity |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.9 % | 1.9 % | Film; ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; Film; ASTM D2457 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 5.5 | 5.5 | Frequency Not Specified |
| Dissipation Factor | 0.21 | 0.21 | Frequency Not Specified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 215 °C | 419 °F | Die temperature |