EPICHEM Epilac R ABS 10% GF Acrylonitrile Butadiene Styrene, 10% Glass Fiber
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | EPICHEM srl |
| Trade Name | Epilac |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epilac R ABS 10% GF Acrylonitrile Butadiene Styrene, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: 10% glass fibre filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638, ISO R527 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638, ISO R527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.300 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
0.562 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256, ISO 180/4a |
| 0.500 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
0.937 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ASTM D256, ISO 180/4a | |
| 0.800 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | >= 80.0 °C | >= 176 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 106 °C @Load 0.999 kg |
223 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 3.20 mm |
1200 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.2 @Frequency 1000 Hz |
3.2 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 500 V | 500 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- NYCOA 2012 Copolymer Nylon
- MV Labs FE165 K4Fe(CN)6·xH2O Potassium ferrocyanide(II) hydrate
- MV Labs SC400 ScCl3·xH2O Scandium chloride hydrate
- Parker Chomerics Tecknit Consil®-E 811 Extruded Silver-Filled Silicone Elastomer
- Hong Kun Group Rhein Pharmaceutical Intermediate
- Indium Corp. Indalloy 220 Silver Solder Alloy
- Indium Corp. NanoFoil® NF40 Nickel and Aluminum Localized Heat Source For Bonding
- Polyram Polytron P30N11 Polypropylene, 30% Long Fiber Glass
- Eurostar Staramide RFC16 PA66/6, Glass/Carbon Fiber Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved