POLYMER SEARCH

EMS-Grivory Grivory® XE 4164 black 9225 PA*-GF30

Category	Polymer , Thermoplastic , Nylon
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® XE 4164 black 9225 PA*-GF30.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory XE 4164 black 9225 is a 30% glass fiber reinforced engineering thermoplastic material based on a semicrystalline, partially aromatic copolyamide. ISO polymer designation: PA 10T/X ASTM designation: PPA, polyphthalamide The main distinguishing features of Grivory HT, when compared to other polyamides, are its good performance at high temperatures providing parts, which are stiffer, stronger, have better heat distortion and dimensional stability as well as excellent chemical resistance and low moisture absorption. Grivory XE 4164 black 9225 is especially suitable for injection molded components in electrical and electronic applications. The material is suitable for lead-free SMT reflow soldering e.g. JEDEC J-STD-020C (peak temperature 260°C). Components conforming to JEDEC MSL1 are achievable.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	ISO 1183
Water Absorption	3.5 %	3.5 %	ISO 62
Moisture Absorption	1.60 %	1.60 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	264 MPa	38300 psi	conditioned; ISO 2039-1
	271 MPa	39300 psi	dry; ISO 2039-1
Tensile Strength at Break	150 MPa	21800 psi	dry; ISO 527-1/-2
	150 MPa	21800 psi	conditioned; ISO 527-1/-2
Elongation at Break	1.8 %	1.8 %	dry; ISO 527-1/-2
	1.8 %	1.8 %	conditioned; ISO 527-1/-2
Tensile Modulus	10.5 GPa	1520 ksi	conditioned; ISO 527-1/-2
	10.5 GPa	1520 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	4.00 J/cm²	19.0 ft-lb/in²	dry; ISO 179/1eU
	4.00 J/cm²	19.0 ft-lb/in²	conditioned; ISO 179/1eU
	3.50 J/cm² @Temperature 30.0 °C	16.7 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	3.50 J/cm² @Temperature 30.0 °C	16.7 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	dry; ISO 179/1eA
	1.00 J/cm²	4.76 ft-lb/in²	conditioned; ISO 179/1eA
	0.800 J/cm² @Temperature 30.0 °C	3.81 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.800 J/cm² @Temperature 30.0 °C	3.81 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	70.0 µm/m-°C	38.9 µin/in-°F	ISO 11359-1/-2
Melting Point	316 °C	601 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	150 °C	302 °F	long term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	275 °C	527 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	140 °C	284 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	dry; IEC 60093
	1.00e+11 ohm-cm	1.00e+11 ohm-cm	conditioned; IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Strength	30.0 kV/mm	762 kV/in	conditioned; IEC 60243-1
	32.0 kV/mm	813 kV/in	dry; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Air intake sytems
	Compressed air systems
	Cooling and climate control
	Fuel systems
	Hydraulic systems
	Interior
	Powertrain and Chassis
Electricals & Electronics	Connectors
	Electrical appliances
	Electrical equipment
	Energy distribution
	Mobile phones and other portable devices
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Tools & Accessories
Processing	Injection Molding
Product Attributes	Bio based Polyamide
	Co Polyamide
	Hydrolysis resistant
	Improved alcohol resistance
	Improved flowability and demoulding
	Partially aromatic Polyamide
Special Characteristics	Improved heat resistance

Users viewing this material also viewed the following: