EMS-Grivory Grivory® XE 4134 black 9225 PA*-GF30
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® XE 4134 black 9225 PA*-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product description: Grivory XE 4134 is a 30% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. ISO polymer designation: PA 10T/X ASTM designation: PPA, polyphthalamide. This Grivory HT product is partially based on renewable raw materials. The main distinguishing features of Grivory HT-PPA, when compared to other polyamides, are its good performance at high temperatures providing parts which are stiffer, stronger, have better heat distortion and dimensional stability as well as excellent chemical resistance and low moisture absorption. Grivory XE 4134 possesses improved flow properties and is especially suitable for low warpage injection molded components in electrical and electronic applications. The material is suitable for lead-free SMT reflow soldering (peak temperature 260°C). Components conforming to JEDEC J-STD-020CMSL1 are achievable.Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 % | 2.0 % | ISO 62 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 240 MPa | 34800 psi | dry; ISO 2039-1 |
| 240 MPa | 34800 psi | conditioned; ISO 2039-1 | |
| Tensile Strength at Break | 140 MPa | 20300 psi | conditioned; ISO 527-1/-2 |
| 145 MPa | 21000 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 1.6 % | 1.6 % | conditioned; ISO 527-1/-2 |
| 1.8 % | 1.8 % | dry; ISO 527-1/-2 | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | conditioned; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | dry; ISO 179/1eU |
| 3.00 J/cm² | 14.3 ft-lb/in² | conditioned; ISO 179/1eU | |
| 3.00 J/cm² @Temperature 30.0 °C |
14.3 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 3.00 J/cm² @Temperature 30.0 °C |
14.3 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | dry; ISO 179/1eA |
| 1.10 J/cm² | 5.23 ft-lb/in² | conditioned; ISO 179/1eA | |
| 1.10 J/cm² @Temperature 30.0 °C |
5.23 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 1.10 J/cm² @Temperature 30.0 °C |
5.23 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | long term; EMS |
| 250 °C | 482 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 165 °C | 329 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | dry; IEC 60093 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | dry; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | conditioned; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Air intake sytems | |
| Compressed air systems | ||
| Fuel systems | ||
| Hydraulic systems | ||
| Interior | ||
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical equipment | |
| Form | Granules | |
| Industry & Consumer goods | Hydraulics & Pneumatics | |
| Mechanical Engineering | ||
| Power transmission | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Product Attributes | Bio based Polyamide | |
| Co Polyamide | ||
| Hydrolysis resistant | ||
| Improved alcohol resistance | ||
| Partially aromatic Polyamide | ||
| Special Characteristics | Anti-static | |
| Improved heat resistance |