EMS-Grivory Grivory® XE 4102 black 9238 PA*-CF30

Category Polymer , Thermoplastic , Nylon
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® XE 4102 black 9238 PA*-CF30.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grivory XE 4102 is a 30% carbon fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partially based on renewable raw materials. ISO polymer designation: PA 10T/X. ASTM designation: PPA, polyphthalamide Grivory XE 4102 is an injection molding material. It has a low density and is electrically conducting The main distinguishing feature of Grivory HT, when compared to other polyamides, is its good performance at high temperatures. Parts made of Grivory HT provide high stiffness and heat distortion temperatures. Further attributes of Grivory HT are the low moisture absorption, good dimensional stability and excellent chemical resistance.Information provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ISO 1183
Water Absorption 2.5 %
2.5 %
ISO 62
Moisture Absorption 1.20 %
1.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 250 MPa
36300 psi
dry; ISO 2039-1
250 MPa
36300 psi
conditioned; ISO 2039-1
Tensile Strength at Break 250 MPa
36300 psi
dry; ISO 527-1/-2
250 MPa
36300 psi
conditioned; ISO 527-1/-2
Elongation at Break 2.0 %
2.0 %
dry; ISO 527-1/-2
2.0 %
2.0 %
conditioned; ISO 527-1/-2
Tensile Modulus 23.0 GPa
3340 ksi
conditioned; ISO 527-1/-2
23.0 GPa
3340 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
dry; ISO 179/1eU
6.00 J/cm²
28.6 ft-lb/in²
conditioned; ISO 179/1eU
6.00 J/cm²

@Temperature 30.0 °C
28.6 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
6.00 J/cm²

@Temperature 30.0 °C
28.6 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
dry; ISO 179/1eA
0.800 J/cm²
3.81 ft-lb/in²
conditioned; ISO 179/1eA
0.600 J/cm²

@Temperature 30.0 °C
2.86 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
0.600 J/cm²

@Temperature 30.0 °C
2.86 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C
5.56 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359-1/-2
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 150 °C
302 °F
long term; EMS
250 °C
482 °F
short term; EMS
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 210 °C
410 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 5000 ohm-cm
5000 ohm-cm
dry; IEC 60093
5000 ohm-cm
5000 ohm-cm
conditioned; IEC 60093
Surface Resistance 15 ohm
15 ohm
IEC 60093
Dielectric Strength 3.00 kV/mm
76.2 kV/in
dry; IEC 60243-1
3.00 kV/mm
76.2 kV/in
conditioned; IEC 60243-1
Descriptive Properties Value Comments
Automotive Powertrain and Chassis
Electricals & Electronics Electrical equipment
Form Granules
Industry & Consumer goods Hydraulics & Pneumatics
Mechanical Engineering
Sanitary, water and gas supply
Processing Injection Molding
Product Attributes Bio based Polyamide
Co Polyamide
Hydrolysis resistant
Improved alcohol resistance
Partially aromatic Polyamide
Special Characteristics Improved heat resistance