EMS-Grivory Grivory® TSC-20/4 EC black 9832 PA666-CF20
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSC-20/4 EC black 9832 PA666-CF20.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | ISO 62 |
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | conditioned; ISO 527-1/-2 |
| 230 MPa | 33400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | conditioned; ISO 527-1/-2 |
| 16.0 GPa | 2320 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | dry; ISO 179/1eU |
| 9.00 J/cm² | 42.8 ft-lb/in² | conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | dry; ISO 179/1eA |
| 1.50 J/cm² | 7.14 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS |
| 200 °C | 392 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 185 °C | 365 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+7 ohm-cm | 1.00e+7 ohm-cm | dry; IEC 60093 |
| 1.00e+7 ohm-cm | 1.00e+7 ohm-cm | conditioned; IEC 60093 | |
| Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Automotive electr. and electronics, lighting | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical appliances | |
| Electrical equipment | ||
| Form | Granules | |
| Industry & Consumer goods | Mechanical Engineering | |
| Power transmission | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Product Attributes | Improved friction & wear properties | |
| Special Characteristics | Anti-static |
Users viewing this material also viewed the following:
- North Wood Plastics PS with 20% Wood Fiber
- Ineos ABS Lustran® QE 1094 AS General Purpose, High-Impact (discontinued **)
- Greene Tweed CHEMRAZ® 513 Perfluoroelastomer
- SABIC Innovative Plastics NORYL TPN9221 PPE+PS (Asia Pacific)
- Shanghai Ofluorine M-1 PVDF Molding Grade
- EMS-Grivory Grivory® TSGL-50-4 nat PA666-GF50
- Chi Mei Polylac® PA-747 ABS
- Dow SiLK™ I 620 Semiconductor Dielectric Resin
- Adell AJ-17 Nylon 66, 35% Glass Reinforced; High Impact
Copyright © lookpolymers.com All Rights Reserved