EMS-Grivory Grivory® TS FR PA666 FR
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TS FR PA666 FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 8.0 % | 8.0 % | ISO 62 |
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
| 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 20 % | 20 % | dry; ISO 527-1/-2 |
| 20 % | 20 % | dry; ISO 527-1/-2 | |
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.20 GPa | 174 ksi | conditioned; ISO 527-1/-2 |
| 3.30 GPa | 479 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
| NB | NB | conditioned; ISO 179/1eU | |
| 8.00 J/cm² @Temperature 30.0 °C |
38.1 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| 1.00 J/cm² @Temperature 30.0 °C |
4.76 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 | V-2 | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | conditioned; IEC 60243-1 |
| 29.0 kV/mm | 737 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 575 V | 575 V | conditioned; IEC 60112 |
| 600 V | 600 V | dry; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Burning Behaviour | VDE | |
| Electricals & Electronics | Connectors | |
| Electrical equipment | ||
| Energy distribution | ||
| Form | Granules | |
| Processing | Injection Molding | |
| Special Characteristics | Flame retardant |
Users viewing this material also viewed the following:
- M. Holland Company CP100 Polypropylene Impact Copolymer
- Kuraray Genestarâ„¢ N1000A-M41 Nylon
- Solvay TECHNYL® C 206 PA6, Conditioned
- Sharadaa Ceramics PCF60-1 Precast Prefired Brick
- A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene
- ChevronTexaco 17 SG 2000 Diesel Engine Oil
- DuPont Performance Polymers Zytel® HTN 51G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
- Axiall 38900 Wire & Cable Flexible PVC
- BCC Products EB 6200 Epoxy Tooling Board
- PolyOne Edgetek® MP-1000 Modified PPO - Unreinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved