EMS-Grivory Grivory® HT2VZ-33H PA6T/66-GF33

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® HT2VZ-33H PA6T/66-GF33.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory HT2VZ-33H is a 33% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT2VZ-33H is an injection molding material. The main distinguishing feature of Grivory HT, when compared to other polyamides, is good performance at high temperatures providing parts which are stiffer, stronger and have better heat distortion stability and chemical resistance. Grivory HT is suitable for production of technical parts in the application fields of: ElectroElectronicsAutomotiveSafety technologyMechanical engineeringInformation provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/in³	ISO 1183
Water Absorption	5.0 %	5.0 %	ISO 62
Moisture Absorption	2.00 %	2.00 %	ISO 62
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	240 MPa	34800 psi	conditioned; ISO 2039-1
	260 MPa	37700 psi	dry; ISO 2039-1
Tensile Strength at Break	180 MPa	26100 psi	conditioned; ISO 527-1/-2
	200 MPa	29000 psi	dry; ISO 527-1/-2
Elongation at Break	2.5 %	2.5 %	dry; ISO 527-1/-2
	2.5 %	2.5 %	conditioned; ISO 527-1/-2
Tensile Modulus	11.0 GPa	1600 ksi	conditioned; ISO 527-1/-2
	11.0 GPa	1600 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	dry; ISO 179/1eU
	5.50 J/cm²	26.2 ft-lb/in²	conditioned; ISO 179/1eU
	4.50 J/cm² @Temperature 30.0 °C	21.4 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
	5.00 J/cm² @Temperature 30.0 °C	23.8 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	dry; ISO 179/1eA
	1.00 J/cm²	4.76 ft-lb/in²	conditioned; ISO 179/1eA
	0.900 J/cm² @Temperature 30.0 °C	4.28 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.900 J/cm² @Temperature 30.0 °C	4.28 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	60.0 µm/m-°C	33.3 µin/in-°F	ISO 11359-1/-2
Melting Point	310 °C	590 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	140 °C	284 °F	long term; EMS
	240 °C	464 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	285 °C	545 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	dry; IEC 60093
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Strength	37.0 kV/mm	940 kV/in	conditioned; IEC 60243-1
	38.0 kV/mm	965 kV/in	dry; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Automotive electr. and electronics, lighting
	Exterior
	Fuel systems
	Interior
	Powertrain and Chassis
Electricals & Electronics	Connectors
	Electrical equipment
Form	Granules
Industry & Consumer goods	Housewares
	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Sports & Leisure
	Tools & Accessories
Processing	Injection Molding
Special Characteristics	High impact or impact modified
	Improved heat resistance
	Improved UV resistance (outdoor use)