EMS-Grivory Grivory® HB 5299 HV PA*

Category	Polymer , Thermoplastic , Nylon
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® HB 5299 HV PA*.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grivory HB 5299 HV is a lubricated, lactam free copolyamide, especially developed for high barrier (oxygen, carbon dioxide) packaging solutions. HV indicates high viscosity, suitable for blown film- and extrusion blow molding applications. Excellent oxygen and carbon dioxide barrier, especially in interaction with moisture (50 up to 100% relative humidity)Excellent transparency, even for thicker ComponentsSuitable as a middle layer in multi-layer films and componentsSuitable for co-extruded and oriented multilayer films in conjunction with all polyamides, polyesters and polyolefinsBarrier properties are hardly affected by steam sterilization. Transparency depends on layer structure and other polymers used. Application: Grivory HB 5299 HV is used in various multi layer structures providing high barrier (oxygen, carbon dioxide, nitrogen, …) e.g. Co-extruded blown films and EBM containersInformation provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/in³	ISO 1183
Water Absorption	5.5 %	5.5 %	ISO 62
Moisture Absorption	2.00 %	2.00 %	ISO 62
Water Vapor Transmission	6.00 g/m²/day	0.386 g/100 in²/day	23°C/85%r.h.; DIS 15106-1/-2
Oxygen Transmission Rate	4.00 cc/m²/day	0.258 cc/100 in²/day	23°C/0%r.h.; DIS 15105-1/-2
	4.00 cc/m²/day	0.258 cc/100 in²/day	23°C/85%r.h.; DIS 15105-1/-2
Carbon Dioxide Transmission	15.0 cc-mm/m²-24hr-atm	38.1 cc-mil/100 in²-24hr-atm	23°C/85%r.h.; DIS 15105-1/-2
	15.0 cc-mm/m²-24hr-atm	38.1 cc-mil/100 in²-24hr-atm	23°C/0%r.h.; DIS 15105-1/-2
Melt Flow	30 g/10 min	30 g/10 min	(MVR) [cm³/10min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	4.5 %	4.5 %	ISO 527-3
Film Elongation at Break, TD	3.5 %	3.5 %	ISO 527-3
Tensile Modulus	4.00 GPa	580 ksi	dry; ISO 527-1/-2
	4.00 GPa	580 ksi	dry; ISO 527-1/-2
Elmendorf Tear Strength MD	510 g	510 g	ISO 6383-2
Elmendorf Tear Strength TD	510 g	510 g	ISO 6383-2
Film Tensile Strength at Break, MD	110 MPa	16000 psi	ISO 527-3
Film Tensile Strength at Break, TD	100 MPa	14500 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	218 °C	424 °F	10°C/min; ISO 11357-1/-3

Optical Properties	Metric	English	Comments
Gloss	150 %	150 %	60°; ISO 2813

Descriptive Properties	Value	Comments
Food contact	EU Requirements
	FDA
Form	Granules
Packaging	Blow moulded containers
	Injectionstretchblowmoulded containers
	Medical packaging
	Non oriented film
	Oriented film
	Paper coating
	Tubes
Processing	Blown Film Extrusion
	Extrusion - blow molding
	Film Extrusion
	Other Extrusion
Product Attributes	Barrier Properties
	High viscosity
	Partially aromatic Polyamide
	Transparent Polyamide
Special Characteristics	Transparent