EMS-Grivory Grivory® G 21 PA6I/6T

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® G 21 PA6I/6T.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Grivory G 21 natural 6506 is a high viscosity, partially aromatic, amorphous copolyamide with processing aid. Improved gas and aroma barrier at elevated relative humidityExcellent flavor and aroma barrierGood Barrier against UV-radiationHighly transparentHigh surface glossGood chemical resistanceVery good abrasion resistance Application examples: Grivory G 21 natural 6506 is suitable as well for the manufacture of coextruded blown film, mono or coex cast film and coextruded tubes as the production of mono and multilayer containers. Grivory G 21 natural 6506 is also used as an additive for polyamide 6 and different copolyamides to improve film properties. Barrier layer for mono- or co-extruded rigid packaging (EBM or ISBM bottles).Information provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 7.0 %
7.0 %
ISO 62
Moisture Absorption 2.00 %
2.00 %
ISO 62
Water Vapor Transmission 7.00 g/m²/day
0.451 g/100 in²/day
23°C/85%r.h.; DIS 15106-1/-2
Oxygen Transmission Rate 10.0 cc/m²/day
0.644 cc/100 in²/day
23°C/85%r.h.; DIS 15105-1/-2
30.0 cc/m²/day
1.93 cc/100 in²/day
23°C/0%r.h.; DIS 15105-1/-2
Carbon Dioxide Transmission 40.0 cc-mm/m²-24hr-atm
102 cc-mil/100 in²-24hr-atm
23°C/85%r.h.; DIS 15105-1/-2
90.0 cc-mm/m²-24hr-atm
229 cc-mil/100 in²-24hr-atm
23°C/0%r.h.; DIS 15105-1/-2
Melt Flow 25 g/10 min
25 g/10 min
(MVR) [cm³/10min]; ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 85.0 MPa
12300 psi
ISO 527-3
Film Tensile Strength at Yield, TD 85.0 MPa
12300 psi
ISO 527-3
Film Elongation at Break, MD 300 %
300 %
ISO 527-3
Film Elongation at Break, TD 300 %
300 %
ISO 527-3
Film Elongation at Yield, MD 5.0 %
5.0 %
ISO 527-3
Film Elongation at Yield, TD 5.0 %
5.0 %
ISO 527-3
Tensile Modulus 3.00 GPa
435 ksi
conditioned; ISO 527-1/-2
3.00 GPa
435 ksi
dry; ISO 527-1/-2
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
dry; ISO 179/1eA
0.800 J/cm²
3.81 ft-lb/in²
conditioned; ISO 179/1eA
0.200 J/cm²

@Temperature 30.0 °C
0.952 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
0.800 J/cm²

@Temperature 30.0 °C
3.81 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
Tear Strength 5.00 kN/m
28.5 pli
Trouser Tear resistance MD; ISO 6383-1
5.00 kN/m
28.5 pli
Trouser Tear resistance TD; ISO 6383-1
Elmendorf Tear Strength MD 1020 g
1020 g
ISO 6383-2
Elmendorf Tear Strength TD 1020 g
1020 g
ISO 6383-2
Film Tensile Strength at Break, MD 85.0 MPa
12300 psi
ISO 527-3
Film Tensile Strength at Break, TD 85.0 MPa
12300 psi
ISO 527-3
Thermal Properties Metric English Comments
Transformation Temperature, Tg 125 °C
257 °F
10°C/min; ISO 11357-1/-2
Optical Properties Metric English Comments
Gloss 160 %
160 %
60°; ISO 2813
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Descriptive Properties Value Comments
Food contact EU Requirements
FDA
Form Granules
Medical USP VI
Packaging Blow moulded containers
Cosmetics / Personal care
Injectionstretchblowmoulded containers
Non oriented film
Oriented film
Paper coating
Tubes
Processing Blown Film Extrusion
Extrusion - blow molding
Film Extrusion
Injection Molding
Other Extrusion
Product Attributes Barrier Properties
Partially aromatic Polyamide
Special Characteristics Transparent