EDRO #5 H13-Hot Work Tool Steel

Category Metal , Ferrous Metal , Chrome-moly Steel , Tool Steel , Hot Work Steel
Manufacturer EDRO
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EDRO #5 H13-Hot Work Tool Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EDRO #5™ H13 is a chromium-molybdenum-vanadium-alloyed steel characterized by: good resistance to thermal shock and thermal fatigue, good high-temperature strength, good toughness and ductility, good machinability, good polishability, good through-hardening properties, and good size stability during hardening.Information provided by EDRO
Mechanical Properties Metric English Comments
Hardness, Brinell 185
185
Delivery condition (soft annealed)
Hardness, Vickers 950 - 1000

@Treatment Temp. 570 °C
950 - 1000

@Treatment Temp. 1060 °F
Tufftride process, 2 hr
1000 - 1250

@Treatment Temp. 525 °C
1000 - 1250

@Treatment Temp. 977 °F
Nitriding in ammonia gas
Tensile Strength, Ultimate 1420 MPa

@Temperature 20.0 °C
206000 psi

@Temperature 68.0 °F
45 HRC
1810 MPa

@Temperature 20.0 °C
263000 psi

@Temperature 68.0 °F
52 HRC
Tensile Strength, Yield 1280 MPa

@Temperature 20.0 °C
185000 psi

@Temperature 68.0 °F
45 HRC
1520 MPa

@Temperature 20.0 °C
220000 psi

@Temperature 68.0 °F
52 HRC
Elongation at Yield 10 %

@Temperature 20.0 °C
10 %

@Temperature 68.0 °F
in 2", 52 HRC
12 %

@Temperature 20.0 °C
12 %

@Temperature 68.0 °F
in 2", 45 HRC
Reduction of Area 45 %

@Temperature 20.0 °C
45 %

@Temperature 68.0 °F
52 HRC
55 %

@Temperature 20.0 °C
55 %

@Temperature 68.0 °F
45 HRC
Component Elements Properties Metric English Comments
Carbon, C 0.40 %
0.40 %
Chromium, Cr 5.3 %
5.3 %
Iron, Fe 90.5 %
90.5 %
As Balance
Manganese, Mn 0.40 %
0.40 %
Molybdenum, Mo 1.4 %
1.4 %
Silicon, Si 1.0 %
1.0 %
Vanadium, V 1.0 %
1.0 %
Descriptive Properties Value Comments
Color Code Green