- Polycarbonate/ABS Alloy, Unreinforced
- E-Polymers Tekaloy® G70NH Non-Halogen Flame Retardant, Un-Reinforced PC/ABS Alloy
E-Polymers Tekaloy® G70NH Non-Halogen Flame Retardant, Un-Reinforced PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKALOY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers Tekaloy® G70NH Non-Halogen Flame Retardant, Un-Reinforced PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non Halogen Flame Retardant, High FlowInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 3.80 J/cm | 7.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 215 - 265 °C | 419 - 509 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
Users viewing this material also viewed the following:
- PolyOne Elastamax™ XL-2165 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Mitsubishi Iupilon® H2000R 23 MFI Polycarbonate With Release
- A. Schulman POLYBATCH™ Green 3015 Concentrate Based In Polyethylene
- Tra-Con Tra-Bond 293-1.5T General Purpose Instrument Epoxy Adhesive-Flexible
- Dow Corning XIAMETER® PMCPMEM-1171 Emulsion
- Covestro Makrolon® Rx2530 Polycarbonate
- Abatron AboCoat 8709-3 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- Ashley Polymers Ashlene® 980LS-40G Nylon 612, 40% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved