E-Polymers TEKAMID® TB110HI , High Impact PA6, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® TB110HI , High Impact PA6, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Impact resistance at low temperatureInformation provided by E-Polymers Co. Ltd.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ASTM D792
Water Absorption 1.4 %
1.4 %
23°C/24 hr; ASTM D570
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D786
Tensile Strength, Yield 65.0 MPa
9430 psi
ASTM D638
Elongation at Break 100 %
100 %
ASTM D638
Flexural Yield Strength 70.0 MPa
10200 psi
ASTM D790
Flexural Modulus 1.90 GPa
276 ksi
ASTM D790
Izod Impact, Notched 4.00 J/cm
7.49 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
 NB

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 20.0 °C
 44.4 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Melting Point 220 °C
428 °F
ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Arc Resistance 180 sec
180 sec
Tungsten electrode; ASTM D495
Processing Properties Metric English Comments
Processing Temperature 245 - 260 °C
473 - 500 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F