E-Polymers TEKAMID® JN910 PPE+PA66 10% Glass Fiber Reinforced PA/PPE Alloy

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® JN910 PPE+PA66 10% Glass Fiber Reinforced PA/PPE Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.JN-series: PA66/PPE, PA6/PPE alloy (Unreinforced, GF reinforced, MF reinforced)Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength 94.176 MPa
13659 psi
ASTM D638
Elongation at Break 11 %
11 %
ASTM D638
Flexural Strength 163.14 MPa
23661 psi
ASTM D790
Flexural Modulus 4.1614 GPa
603.56 ksi
ASTM D790
Izod Impact, Notched 0.814 J/cm
1.52 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 280 - 305 °C
536 - 581 °F
Mold Temperature 75.0 - 120 °C
167 - 248 °F