E-Polymers SEPAZ® K140HF 40% Glass Fiber Reinforced Low Flash, High Flow PPS Resin

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer E-Polymers Co. Ltd.
Trade Name SEPAZ®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers SEPAZ® K140HF 40% Glass Fiber Reinforced Low Flash, High Flow PPS Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide Resin: High-performance engineering plastic SEPAZ PPS boasts excellent high-temperature resistance, flame retardancy and chemical resistance, physical strength, and its fluidity leads to good dimensional precision. SEPAZ PPS applications: switches, connectors and other electronic and electric components, alternators and other automobile components, and office equipment components including chassis parts and housings.Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.67 g/cc
1.67 g/cc
ASTM D792
Water Absorption 0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength 181.5 MPa
26320 psi
ASTM D638
Elongation at Break 2.2 %
2.2 %
ASTM D638
Flexural Strength 269.78 MPa
39128 psi
ASTM D790
Flexural Modulus 13.7 GPa
1990 ksi
ASTM D790
Izod Impact, Notched 0.883 J/cm
1.65 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 23.0 µm/m-°C

@Thickness 1.60 mm
12.8 µin/in-°F

@Thickness 0.0630 in
ASTM D696
CTE, linear, Transverse to Flow 32.0 µm/m-°C

@Thickness 1.60 mm
17.8 µin/in-°F

@Thickness 0.0630 in
ASTM D696
Melting Point 278 °C
532 °F
ASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 266 °C
511 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm

@Thickness 1.60 mm
483 kV/in

@Thickness 0.0630 in
ASTM D149
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 300 - 330 °C
572 - 626 °F
Mold Temperature 130 - 160 °C
266 - 320 °F
Drying Temperature 140 °C
284 °F
Dry Time 6 hour
6 hour