E-Polymers SEPAZ® C130M 30% Mineral Reinforced LCP Resin

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), Mineral Filled
Manufacturer E-Polymers Co. Ltd.
Trade Name SEPAZ®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers SEPAZ® C130M 30% Mineral Reinforced LCP Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding productivity. SEPAZ LCP has a unique attribute in that the thinner the product becomes, the greater the mechanical strength. SEPAZ LCP finds uses in connectors, sensors and other electronic components and CD pick-up parts, and in copying machine and fax components in office and audio-visual equipment.Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.63 g/cc
1.63 g/cc
ASTM D792
Linear Mold Shrinkage 0.00 cm/cm
0.00 in/in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength 127.53 MPa
18497 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Flexural Strength 127.53 MPa
18497 psi
ASTM D790
Flexural Modulus 9.6138 GPa
1394.4 ksi
ASTM D790
Thermal Properties Metric English Comments
CTE, linear 8.00 µm/m-°C

@Thickness 1.60 mm
4.44 µin/in-°F

@Thickness 0.0630 in
ASTM D696
CTE, linear, Transverse to Flow 22.0 µm/m-°C

@Thickness 1.60 mm
12.2 µin/in-°F

@Thickness 0.0630 in
ASTM D696
Melting Point 335 °C
635 °F
ASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 239 °C
462 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 26.0 kV/mm

@Thickness 1.60 mm
660 kV/in

@Thickness 0.0630 in
ASTM D149
Dissipation Factor 0.028

@Frequency 1.00e+6 Hz
0.028

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 350 - 360 °C
662 - 680 °F
Mold Temperature 30.0 - 150 °C
86.0 - 302 °F