DuPont Vamac® HVG Sample Compound
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Vamac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Vamac® HVG Sample Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Test compound is press cured for 5 minutes at 175°C and post cured for 4 hours at 175°C.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 55 @Temperature 100 °C |
55 @Temperature 212 °F |
ML(1+4); ASTM D1646 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | ASTM D2240 |
| Tensile Strength, Ultimate | 16.4 MPa | 2380 psi | ASTM D412 |
| Elongation at Break | 275 % | 275 % | ASTM D412 |
| 100% Modulus | 0.00600 GPa | 0.870 ksi | ASTM D412 |
| Compression Set | 16 % | 16 % | 70 hrs at 150°C; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Armeen® 18D | 0.5 phr | |
| Diak No. 1 | 1.5 phr | |
| DOTG Coaccelerator | 4 phr | |
| Mooney Scorch at 121°C, Minimum Viscosity | 23.4 metric minutes | Mooney Units, ASTM D1646 |
| Mooney Scorch at 121°C, t10 | 10.5 metric minutes | Time for 10 unit rise, ASTM D1646 |
| Mooney Scorch at 121°C, t18 | 17.6 metric minutes | Time for 18 unit rise, ASTM D1646 |
| N550 Black | 60 phr | |
| Naugard® 445 antioxidant | 2 phr | |
| Stearic Acid | 1.5 phr | |
| TP-761 | 10 phr | |
| Vamac® HVG | 100 phr | |
| Vanfre® VAM | 1.5 phr |