DuPont Teijin Films Mylar® RSX951 Polyester Film, 175 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® RSX951 Polyester Film, 175 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production process, providing excellent adhesion of the coating to the polyester film for improved liner performance.Mylar® RSX951 has balanced tensile properties and good dimensional stability. Release values typically range between 15 and 25 grams per inch when tested with aggressive pressure-sensitive adhesives. It is recommended that the liner be tested in each application to verify the absolute value of the release strength.Information provided by DuPont.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
Typical Mylar®; ASTM D1505
Coating Weight 0.0720 g/m²
0.0450 lb/ream
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 150 %
150 %
ASTM D882A
Film Elongation at Break, TD 115 %
115 %
ASTM D882A
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
Film Tensile Strength at Break, TD 234 MPa
34000 psi
ASTM D882A
Heat Seal Strength >= 22.0 g/25 mm
>= 0.0485 lb/in
Using Tesa 7475 Tape
Thermal Properties Metric English Comments
Specific Heat Capacity 1.17 J/g-°C
0.280 BTU/lb-°F
Typical Mylar®
Melting Point 254 °C
489 °F
Typical Mylar® via DSC
Shrinkage, MD 2.3 %

@Temperature 150 °C,
Time 1800 sec
2.3 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Shrinkage, TD 0.50 %

@Temperature 150 °C,
Time 1800 sec
0.50 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Optical Properties Metric English Comments
Haze 7.5 %
7.5 %
ASTM D1003