DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 100 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 100 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film in packaging frozen and refrigerated foods. Mylar® RL32 is designed to seal to a broad range of container substrates including amorphous polyester (APET, also PETG), semicrystalline polyester (CPET), polyester coated paperboard, polyvinylchloride (PVC), polyethylene (HDPE), polypropylene (PP), and polystyrene (HIPS). Mylar® RL32 has the same type heat seal layer as Mylar® RL31, but the thickness of the heat seal layer and the heat seal strengths of Mylar® RL32 are intermediate between Mylar® RL31 and Mylar® RL33. Mylar® RL32 and Mylar® RL4 produce similar heat seal strengths to most substrates, but Mylar® RL32 has a greater tendency to produce tearing seals while Mylar® RL4 tends to produce more peelable seals. Like Mylar® RL31, Mylar® RL32 has a lower seal initiation temperature than lidding films with an amorphous polyester heat seal layer (e.g., Mylar® OL, OL2). This allows good seals to be made at higher line speeds (or using lower sealing temperatures).
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Calculated from nominal thickness and yield
Moisture Vapor Transmission 0.610 cc-mm/m²-24hr-atm
1.55 cc-mil/100 in²-24hr-atm
Proc. E; ASTM E96
Oxygen Transmission 2.36 cc-mm/m²-24hr-atm
5.99 cc-mil/100 in²-24hr-atm
Tested per ASTM D3985 at 22°C
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
ASTM D882
Film Elongation at Break, TD 80 %
80 %
ASTM D882
Secant Modulus 3.79 GPa
550 ksi
Stiffness Modulus; ASTM D882
Tear Strength Test 1.1
1.1
lb Graves; ASTM D1004
Film Tensile Strength at Break, MD 172 MPa
24900 psi
ASTM D882
Film Tensile Strength at Break, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F