DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 100 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 100 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sealable lidding film in packaging refrigerated and frozen foods. Mylar® OL13 is dual ovenable film which provides very strong, aggressive seals to polar substrates such as amorphous polyester (APET, also PETG), semicrystalline polyester (CPET), polyester coated paperboard, and polyvinylchloride (PVC). Mylar® OL13 does not seal to polyethylene, polypropylene, or polystyrene. DuPont Teijin Films offers another family of lidding films (RL types) for sealing to these substrates. Mylar® OL13 is similar to OL12 but has a thicker seal layer than Mylar® OL12 to give enhanced seal strength. In general, Mylar® OL13 can produce non-peeling, near "lock-up" type seals and is recommended for hot fill applications where non-peeling seals are desired. It can also be used in some "post-pasteurized" (steam sterilization) applications where the pressure balance in the package can be properly controlled (via vacuum or overpressure). Mylar® OL13 lidding films have excellent grease and oil resistance.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Calculated from nominal thickness and yield
Moisture Vapor Transmission 0.610 cc-mm/m²-24hr-atm
1.55 cc-mil/100 in²-24hr-atm
Proc. E; ASTM E96
Oxygen Transmission 2.36 cc-mm/m²-24hr-atm
5.99 cc-mil/100 in²-24hr-atm
Tested per ASTM D3985 at 22°C
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
ASTM D882
Film Elongation at Break, TD 80 %
80 %
ASTM D882
Secant Modulus 3.79 GPa
550 ksi
Stiffness Modulus; ASTM D882
Tear Strength Test 1.1
1.1
lb Graves; ASTM D1004
Film Tensile Strength at Break, MD 172 MPa
24900 psi
ASTM D882
Film Tensile Strength at Break, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
399 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F