DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 100 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 100 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the opposite side of the film from the heat seal layer. Mylar® OB12 is essentially Mylar® OL12 with a barrier layer. Mylar® OB12 is dual ovenable film which provides strong, aggressive seals to polar substrates such as amorphous polyester (APET, also PETG), semicrystalline polyester (CPET), polyester coated paperboard, and polyvinylchloride (PVC). Mylar® OB12 does not seal to polyethylene, polypropylene, or polystyrene. DuPont Teijin Films offers another family of lidding films (RB types) for sealing to these substrates.Mylar® OB12 has higher hot tack and a thicker seal layer than either Mylar® OB02 or OL2, and can be used in hot fill applications. It is not recommended for applications requiring retort sterilization. Mylar® OB12 lidding films have excellent grease and oil resistance. Heat seals produced with Mylar® OB12 are stronger than with Mylar® OL2 and may be difficult to peel without shredding at any gauge. Mylar® OB12 is recommended for applications needing a lidding film which heat seals like Mylar® OL12, but with much lower permeability to gases (oxygen, carbon dioxide) and moisture.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Calculated from nominal thickness and yield
Moisture Vapor Transmission 0.220 cc-mm/m²-24hr-atm
0.559 cc-mil/100 in²-24hr-atm
Proc. E; ASTM E96
Oxygen Transmission 0.220 cc-mm/m²-24hr-atm
0.559 cc-mil/100 in²-24hr-atm
Tested per ASTM D3985 at 22°C
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
ASTM D882
Film Elongation at Break, TD 80 %
80 %
ASTM D882
Secant Modulus 3.79 GPa
550 ksi
Stiffness Modulus; ASTM D882
Tear Strength Test 1.1
1.1
lb Graves; ASTM D1004
Film Tensile Strength at Break, MD 172 MPa
24900 psi
ASTM D882
Film Tensile Strength at Break, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
399 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F