DuPont Teijin Films Melinex® CORE 2 Polyester Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Melinex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Melinex® CORE 2 Polyester Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Melinex® CORE 2 is a two-side heat sealable, opaque white polyester film which is ideal in specialty card laminate applications. This film can be heat sealed to itself and other polyesters, as well as a variety of substrates including some grades of paper, PVC, and Teslin®. The film is supplied with heat seal surfaces modified to prevent air entrapment during lamination. The heat seal co-polyester layer will accept UV curable off-set litho and screen printing inks. Melinex® CORE 2 film is available in 600 to 1210 gauge.Information provided by DuPont.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D1505
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 73.1 MPa
10600 psi
ASTM D882A
Film Tensile Strength at Yield, TD 73.1 MPa
10600 psi
ASTM D882A
Film Elongation at Break, MD 140 %
140 %
ASTM D882A
Film Elongation at Break, TD 110 %
110 %
ASTM D882A
Coefficient of Friction, Dynamic 0.90
0.90
A-B; ASTM D1894
Film Tensile Strength at Break, MD 108 MPa
15600 psi
ASTM D882A
Film Tensile Strength at Break, TD 108 MPa
15600 psi
ASTM D882A
Heat Seal Strength Initiation Temperature 120 - 200 °C
248 - 392 °F
Thermal Properties Metric English Comments
Shrinkage, MD 2.0 %

@Temperature 190 °C,
Time 300 sec
2.0 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Shrinkage, TD 1.0 %

@Temperature 190 °C,
Time 300 sec
1.0 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Optical Properties Metric English Comments
Transmission, Visible 5.0 %

@Thickness 0.254 mm
5.0 %

@Thickness 0.0100 in
TLT; ASTM D1003
7.0 %

@Thickness 0.152 mm
7.0 %

@Thickness 0.00600 in
TLT; ASTM D1003