DuPont Teijin Films Melinex® 514P Polyester Film

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer	DuPont Teijin Films (DTF)
Trade Name	Melinex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Teijin Films Melinex® 514P Polyester Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This high clarity film has one side hydrophilic pretreated to promote adhesion to many solvent coatings formulations, while the opposite side is pretreated to provide antistatic protection.Information provided by DuPont.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	101 MPa	14600 psi	ASTM D882A
Film Tensile Strength at Yield, TD	207 MPa	30000 psi	ASTM D882A
Film Elongation at Break, MD	190 %	190 %	ASTM D882A
Film Elongation at Break, TD	120 %	120 %	ASTM D882A
Coefficient of Friction, Dynamic	0.33	0.33	A-B; ASTM D1894
Film Tensile Strength at Break, MD	181 MPa	26200 psi	ASTM D882A
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A

Thermal Properties	Metric	English	Comments
Shrinkage, MD	2.5 % @Temperature 190 °C, Time 300 sec	2.5 % @Temperature 374 °F, Time 0.0833 hour	Unrestrained
Shrinkage, TD	0.40 % @Temperature 190 °C, Time 300 sec	0.40 % @Temperature 374 °F, Time 0.0833 hour	Unrestrained

Optical Properties	Metric	English	Comments
Transmission, Visible	87.1 % @Thickness 0.165 mm	87.1 % @Thickness 0.00650 in	TLT; ASTM D1003
	87.1 % @Thickness 0.178 mm	87.1 % @Thickness 0.00700 in	TLT; ASTM D1003
	88.5 % @Thickness 0.0914 mm	88.5 % @Thickness 0.00360 in	TLT; ASTM D1003

Electrical Properties	Metric	English	Comments
Surface Resistivity per Square	6.30e+10 ohm @Temperature 23.0 °C	6.30e+10 ohm @Temperature 73.4 °F	100 V DC 66% RH; ASTM D257