DuPont Teijin Films Melinex® 455 Polyester Film

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer	DuPont Teijin Films (DTF)
Trade Name	Melinex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Teijin Films Melinex® 455 Polyester Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Melinex® 455 is a high clarity polyester film pretreated on one side for slip. It has excellent handling characteristics.General Product Info: Two smooth coatable surfacesLow surface resistivityCan be topcoated on either sideImproves safety and cleanlinessApprovals: Library of Congress Specification - This film meets the Library of Congress Specification Number 500-500-5/31/95 for use in archival storage.Information provided by DuPont.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	96.5 MPa	14000 psi	ASTM D882A
Film Tensile Strength at Yield, TD	96.5 MPa	14000 psi	ASTM D882A
Film Elongation at Break, MD	150 %	150 %	ASTM D882A
Film Elongation at Break, TD	100 %	100 %	ASTM D882A
Coefficient of Friction, Dynamic	0.40	0.40	A-B; ASTM D1894
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
Film Tensile Strength at Break, TD	248 MPa	36000 psi	ASTM D882A

Thermal Properties	Metric	English	Comments
Shrinkage, MD	2.5 % @Temperature 190 °C, Time 300 sec	2.5 % @Temperature 374 °F, Time 0.0833 hour	Unrestrained
Shrinkage, TD	1.0 % @Temperature 190 °C, Time 300 sec	1.0 % @Temperature 374 °F, Time 0.0833 hour	Unrestrained

Optical Properties	Metric	English	Comments
Transmission, Visible	87 % @Thickness 0.165 mm	87 % @Thickness 0.00650 in	TLT; ASTM D1003
	88 % @Thickness 0.118 mm	88 % @Thickness 0.00465 in	TLT; ASTM D1003
	88.3 % @Thickness 0.0940 mm	88.3 % @Thickness 0.00370 in	TLT; ASTM D1003
	88.5 % @Thickness 0.0686 mm	88.5 % @Thickness 0.00270 in	TLT; ASTM D1003
	88.7 % @Thickness 0.0508 mm	88.7 % @Thickness 0.00200 in	TLT; ASTM D1003