DuPont Teijin Films Melinex® 197 Polyester Film
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Melinex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Melinex® 197 Polyester Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melinex® 197 is a very clear polyester film with good handling properties, suitable for general purpose applications.Information provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 100 MPa | 14500 psi | ASTM D882A |
| Film Tensile Strength at Yield, TD | 100 MPa | 14500 psi | ASTM D882A |
| Film Elongation at Break, MD | 140 % | 140 % | ASTM D882A |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882A |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | A-B; ASTM D1894 |
| Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | ASTM D882A |
| Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.2 % @Temperature 190 °C, Time 300 sec |
3.2 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Shrinkage, TD | 2.5 % @Temperature 190 °C, Time 300 sec |
2.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.90 % @Thickness 0.0122 mm |
0.90 % @Thickness 0.000480 in |
ASTM D1003 |
| 1.0 % @Thickness 0.234 mm |
1.0 % @Thickness 0.00920 in |
ASTM D1003 | |
| 2.0 % @Thickness 0.0508 mm |
2.0 % @Thickness 0.00200 in |
ASTM D1003 | |
| Transmission, Visible | 87.7 % @Thickness 0.0508 mm |
87.7 % @Thickness 0.00200 in |
TLT; ASTM D1003 |
| 88.2 % @Thickness 0.234 mm |
88.2 % @Thickness 0.00920 in |
TLT; ASTM D1003 | |
| 88.5 % @Thickness 0.0122 mm |
88.5 % @Thickness 0.000480 in |
TLT; ASTM D1003 |
Users viewing this material also viewed the following:
- RheTech Products GC43P250-00 43% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural
- SABIC Innovative Plastics LNP Faradex MS002P PP (Europe-Africa-Middle East)
- Ferro IP 750 Passivation Glasses (Pb-B-Si-Al; Pb-Si-Al; Si-Pb-Al Silicates)
- A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
- Chevron Phillips Marlex® 9346 HDPE Natural Pipe Resin
- Chevron Phillips Marlex® HP076 High Density Polyethylene, Pipe Grade
- BASF Neopolen® P 9235 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- 3M Scotch® 720 Film/Fiber Tape
- Polimeri Europa SINKRAL G323 ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved