DuPont™ Surlyn® PC100 Ionomer Resin, Highest Clarity, Sodium
| Category | Polymer , Thermoplastic , Ionomer , Ionomer, Molded |
| Manufacturer | DuPont |
| Trade Name | Surlyn® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont™ Surlyn® PC100 Ionomer Resin, Highest Clarity, Sodium.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Surlyn® PC100 luxury molding resin is a "select" grade of Surlyn® 8920, controlled to achieve the highest possible optical clarity in molded perfume jars and caps. It complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins. The resin can be injection or blow molded, and is processable by extrusion into sheets or shapes.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.90 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Ultimate | 37.2 MPa | 5400 psi | ASTM D638 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | 50 mm/min cross speed; ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | ASTM D790 |
| Izod Impact, Notched | 6.35 J/cm | 11.9 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 860 kJ/m² | 409 ft-lb/in² | ASTM D1822S |
| Abrasion | 640 | 640 | NBS Index; ASTM D1630 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature -20.0 - 32.0 °C |
77.8 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | |
| Melting Point | 88.0 °C | 190 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
| Vicat Softening Point | 45.0 °C | 113 °F | Rate B, ASTM D1525-70 |
| Flame Spread | 20.3 mm/min | 0.799 in/min | ASTM D635 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % @Thickness 6.35 mm |
4.0 % @Thickness 0.250 in |
ASTM D1003A |
| Gloss | 80 % | 80 % | 20° per ASTM D523-6 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |