DuPont™ Surlyn® 9950 Ionomer Resin, Zinc
| Category | Polymer , Thermoplastic , Ionomer , Ionomer, Molded |
| Manufacturer | DuPont |
| Trade Name | Surlyn® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont™ Surlyn® 9950 Ionomer Resin, Zinc.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Surlyn® 9950 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutralization levels for this grade result in good tear resistance, clarity, and stiffness compared with other grades of Surlyn®. The resin can be injection molded. It complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Ultimate | 28.3 MPa | 4100 psi | ASTM D638 |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min cross speed, ASTM D638 |
| Elongation at Break | 490 % | 490 % | ASTM D638 |
| Flexural Modulus | 0.250 GPa | 36.3 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tensile Impact Strength | 1020 kJ/m² | 485 ft-lb/in² | ASTM D1822S |
| Abrasion | 130 | 130 | NBS Index; ASTM D1630 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 150 µm/m-°C @Temperature -20.0 - 32.0 °C |
83.3 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | |
| Melting Point | 87.0 °C | 189 °F | DTA |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.0 °C | 117 °F | ASTM D648 |
| Vicat Softening Point | 66.0 °C | 151 °F | Rate B, ASTM D1525-70 |
| Brittleness Temperature | -100 °C | -148 °F | ASTM D746 |
| Flame Spread | 27.9 mm/min | 1.10 in/min | ASTM D635 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 18 % @Thickness 6.40 mm |
18 % @Thickness 0.252 in |
ASTM D1003A |
| Gloss | 30 % | 30 % | 20° per ASTM D523-6 |