Material Notes:
Surlyn® 9910 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutralization levels for this grade result in a combination of high clarity, stiffness and abrasion resistance, along with a very low melt flow index of 0.7. The resin can be extruded, blow molded, and injection molded. In golf ball covers, it provides excellent durability, especially when blended with other grades of Surlyn® made with other cations. It complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ASTM D792
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.70 g/10 min

@Load 4.76 lb,
Temperature 374 °F
condition E; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 64
64
ASTM D2240
Tensile Strength, Ultimate 24.8 MPa
3600 psi
ASTM D638
Tensile Strength, Yield 13.8 MPa
2000 psi
50 mm/min cross speed; ASTM D638
Elongation at Break 290 %
290 %
ASTM D638
Flexural Modulus 0.330 GPa
47.9 ksi
ASTM D790
Izod Impact, Notched 3.65 J/cm
6.84 ft-lb/in
ASTM D256
Tensile Impact Strength 1020 kJ/m²
485 ft-lb/in²
ASTM D1822S
Abrasion 610
610
NBS Index; ASTM D1630
Thermal Properties Metric English Comments
CTE, linear 140 µm/m-°C

@Temperature -20.0 - 32.0 °C
77.8 µin/in-°F

@Temperature -4.00 - 89.6 °F
ASTM D696
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
Melting Point 86.0 °C
187 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 44.0 °C
111 °F
ASTM D648
Vicat Softening Point 62.0 °C
144 °F
Rate B, ASTM D1525-70
Brittleness Temperature -105 °C
-157 °F
ASTM D746
Flame Spread 22.9 mm/min
0.902 in/min
ASTM D635
Optical Properties Metric English Comments
Haze 6.0 %

@Thickness 6.35 mm
6.0 %

@Thickness 0.250 in
ASTM D1003A
Gloss 60 %
60 %
20° per ASTM D523-6