- DuPont™ Surlyn® 9730 Ionomer Resin, Zinc (discontinued **)
DuPont™ Surlyn® 9730 Ionomer Resin, Zinc (discontinued **)
| Category | Polymer , Thermoplastic , Ionomer , Ionomer, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont™ Surlyn® 9730 Ionomer Resin, Zinc
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Surlyn® 9730 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutralization levels for this grade result in a combination of toughness, tear resistance, and clarity. The resin can be injection molded or extruded into sheets or shapes. It complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Ultimate | 28.3 MPa | 4100 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | 50 mm/min cross speed; ASTM D638 |
| Elongation at Break | 460 % | 460 % | ASTM D638 |
| Flexural Modulus | 0.210 GPa | 30.5 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tensile Impact Strength | 1240 kJ/m² | 590 ft-lb/in² | ASTM D1822S |
| Abrasion | 360 | 360 | NBS Index; ASTM D1630 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 160 µm/m-°C @Temperature -20.0 - 32.0 °C |
88.9 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 90.0 °C | 194 °F | DTA |
| Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
| Vicat Softening Point | 73.0 °C | 163 °F | Rate B, ASTM D1525-70 |
| Brittleness Temperature | -100 °C | -148 °F | ASTM D746 |
| Flame Spread | 20.3 mm/min | 0.799 in/min | ASTM D635 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 15 % @Thickness 6.40 mm |
15 % @Thickness 0.252 in |
ASTM D1003A |
| Gloss | 25 % | 25 % | 20° per ASTM D523-6 |