DuPont™ Surlyn® 9020 Ionomer Resin, Zinc

Category Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer DuPont
Trade Name Surlyn®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Surlyn® 9020 Ionomer Resin, Zinc.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Surlyn® 9020 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The resin contains an additional co-monomer to facilitate its use as a modifier for toughened grades of nylon 6 and 6/6. The amount of MAA and neutralization levels for this grade are optimized to impart low-temperature toughness. The resin complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
ASTM D792
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
condition E; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 55
55
ASTM D2240
Tensile Strength, Ultimate 26.2 MPa
3800 psi
ASTM D638
Elongation at Break 510 %
510 %
ASTM D638
Flexural Modulus 0.100 GPa
14.5 ksi
ASTM D790
Izod Impact, Notched NB
NB
ASTM D256
Tensile Impact Strength 1280 kJ/m²
609 ft-lb/in²
ASTM D1822S
Abrasion 220
220
NBS Index; ASTM D1630
Thermal Properties Metric English Comments
CTE, linear 170 µm/m-°C

@Temperature -20.0 - 32.0 °C
94.4 µin/in-°F

@Temperature -4.00 - 89.6 °F
ASTM D696
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
Melting Point 81.0 °C
178 °F
DTA
Deflection Temperature at 0.46 MPa (66 psi) 40.0 °C
104 °F
ASTM D648
Vicat Softening Point 57.0 °C
135 °F
Rate B, ASTM D1525-70
Brittleness Temperature -112 °C
-170 °F
ASTM D746
Flame Spread 25.4 mm/min
1.00 in/min
ASTM D635
Optical Properties Metric English Comments
Haze 7.0 %

@Thickness 6.35 mm
7.0 %

@Thickness 0.250 in
ASTM D1003A
Gloss 45 %
45 %
20° per ASTM D523-6