Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

DuPont Surlyn® 1650SB

Category Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate
Manufacturer DuPont Packaging and Industrial Polymers
Trade Name Surlyn®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Surlyn® 1650SB.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DuPont™ Surlyn® 1650SB is available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Slip and antiblock agents are added to reduce the film coefficient of friction and prevent film roll locking. Applications: Meat, poultry, seafood, and cheese packagingCereal linersMedical/pharmaceutical packaging Powdered/granular food and non-food pouches Edible oil, motor oil, and other liquid product pouchesSnack structures Coextrusions with nylon or in other film structures as a heat sealInformation provided by DuPont™
Physical Properties Metric English Comments
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238, ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.20 MPa
5105 psi
MD; ASTM D882
42.1 MPa
6110 psi
TD; ASTM D882
Elongation at Break 350 %
350 %
MD; ASTM D882
350 %
350 %
TD; ASTM D882
Impact 27
27
J/mm, Spencer Impact; ASTM D3420
Elmendorf Tear Strength, MD 13.9 g/micron
353 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 15.1 g/micron
384 g/mil
Dart Drop 9.80 g/micron
249 g/mil
ASTM D1709
1% Secant Modulus, MD 255 MPa
37000 psi
ASTM D882
1% Secant Modulus, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 72.0 °C
162 °F
Freezing Point; ASTM D3418
96.0 °C
205 °F
ASTM D3417- ISO 3146
Vicat Softening Point 73.0 °C
163 °F
ASTM D1525, ISO 306
Optical Properties Metric English Comments
Haze 10.5 %
10.5 %
ASTM D1003
Gloss 20 %
20 %
20°; ASTM D2457
Processing Properties Metric English Comments
Rear Barrel Temperature 149 °C
300 °F
Middle Barrel Temperature 191 °C
376 °F
Front Barrel Temperature 191 °C
376 °F
Die Temperature 191 °C
375 °F